Positive Electrode Active Material For A Lithium-Ion Battery, Positive Electrode For A Lithium-Ion Battery, Lithium-Ion Battery Using Same, And Precursor To A Positive Electrode Active Material For A Lithium-Ion Battery

ABSTRACT

The present invention provides a positive electrode active material for lithium ion batteries, which realizes a lithium ion battery that is, while satisfying fundamental characteristics of a battery (capacity, efficiency, load characteristics), low in the resistance and excellent in the lifetime characteristics. In the positive electrode active material for lithium ion batteries, the variation in the composition of transition metal that is a main component inside of particles of or between particles of the positive electrode active material, which is defined as a ratio of the absolute value of the difference between a composition ratio inside of the particles of or in a small area between the particles of the transition metal and a composition ratio in a bulk state to the composition ratio in a bulk state of the transition metal, is 5% or less.

TECHNICAL FIELD OF THE INVENTION

The present invention relates to a positive electrode active material for lithium ion batteries, a positive electrode for lithium ion batteries and a lithium ion battery therewith, and a precursor for positive electrode active material for lithium ion batteries.

BACKGROUND OF THE INVENTION

In a positive electrode active material for lithium ion batteries, a lithium-containing transition metal oxide is generally used. Specifically, lithium cobalt oxide (LiCoO₂), lithium nickel oxide (LiNiO₂), and lithium manganese oxide (LiMn₂O₄) are cited, and, in order to enhance an improvement in the characteristics (higher capacity, cycle characteristics, storage characteristics, reduction of internal resistance, charge and discharge characteristics) and safety, these have been studied by complexing. In particular, for a lithium ion battery for large devices such as automobiles and road levelers, characteristics different from those for conventional portable telephones and personal computers are demanded. Specifically, the positive electrode active material for use in automobiles is required to be high in capacity and low in the resistance, and the positive electrode active material for use in road levelers is required to be high in the capacity and long in the lifetime.

Powder characteristics are important in order to develop these characteristics. However, homogeneity in distributions of transition metal and lithium that are main components of the positive electrode active material of a lithium ion battery is particularly important. The homogeneity of the composition is particularly indispensable for obtaining low resistance for use in automobiles and the long lifetime for use in road levelers.

In Japanese Patent Application Laid-Open No. 2005-285572 (patent document 1) related to application by Nikko-Materials Co., Ltd (current appellation: JX Nippon Mining & Metals Co., Ltd.), to which the present inventors belong, the following fact was found and reported. That is, as a manufacturing method of a precursor for positive electrode active material, a method in which an aqueous solution of chloride of Ni, Mn or Co is poured into a suspension of lithium carbonate, and, the resulted carbonate is washed with a saturated solution of lithium carbonate or ethanol is used, a molar ratio of an amount of Li to a total amount of metals can be adjusted and the variation thereof can be reduced.

Further, in Japanese Patent Application Laid-Open No. 2001-110420 (patent document 2), it is described that, after studying large secondary particles where small crystalline primary particles are flocculated, and magnitude of particles of lithium carbonate that is a raw material, it was found that a cohesion force is enhanced by controlling the particle size of lithium carbonate, and thereby a positive electrode active material homogeneously reacted not only on a surface of the secondary particles of lithium cobalt oxide but also inside of the secondary particles of lithium cobalt oxide and having excellent discharged capacity characteristics and cycle characteristics can be obtained. Further, it is described that, when such a positive electrode active material is synthesized without variation in composition to the inside of lithium cobalt oxide configured of spherical or elliptical secondary particles in which primary particles of small crystal are flocculated, a positive electrode active material for nonaqueous electrolyte secondary batteries characterized in that not only the primary particles on a surface forming the secondary particle but also the primary particles inside of the secondary particle can be used as a battery. Specifically, it is described that, according to the analysis of sections of secondary particles of lithium cobalt oxide with an electron probe microanalyzer (EPMA), a ratio of spectral intensities of O/Co of oxygen and cobalt inside of the particles is within 3.0±0.5.

-   (Patent documents 1) Japanese Patent Application Laid-Open No.     2005-285572 -   (Patent documents 2) Japanese Patent Application Laid-Open No.     2001-110420

SUMMARY OF THE INVENTION

However, there is still a room for improvement as a positive electrode active material that realizes a lithium ion battery which is, while satisfying fundamental characteristics of a battery (capacity, efficiency, load characteristics), low in the resistance and excellent in the lifetime characteristics.

The invention intends to provide a positive electrode active material for lithium ion batteries, which realizes a lithium ion battery that is, while satisfying fundamental characteristics of a battery (capacity, efficiency, load characteristics), low in the resistance and excellent in the lifetime characteristics. Further, the invention further intends to separately provide a positive electrode for lithium ion batteries which use the positive electrode active material for lithium ion batteries, a lithium ion battery therewith, and a precursor for positive electrode active material for lithium ion batteries.

The present inventors have found, after studying hard by paying attention also to homogeneity other than an amount of Li in a positive electrode active material, that, when a positive electrode active material where the variation in the composition of transition metal that is a main component is controlled in a specified range is used, a lithium ion battery which is, while satisfying fundamental characteristics of a battery (capacity, efficiency, load characteristics), low in the resistance and excellent in the lifetime characteristics can be provided.

The invention completed based on the above findings is in an aspect a positive electrode active material for lithium ion batteries, which is composed of at least lithium and transition metal. In the positive electrode active material for lithium ion batteries, the variation in the composition of transition metal that is a main component inside of particles of or between particles of the positive electrode active material, which is defined as a ratio of the absolute value of the difference between a composition ratio inside of the particles of or in a small area between the particles of the transition metal and a composition ratio in a bulk state to the composition ratio in a bulk state of the transition metal, is 5% or less.

In an embodiment of the positive electrode active material for lithium ion batteries related to the invention, the positive electrode active material is a lithium-containing transition metal oxide.

In another embodiment of the positive electrode active material for lithium ion batteries related to the invention, the transition metal in the lithium-containing transition metal oxide is at least one or two or more kinds selected from the group consisting of Ni, Mn, Co and Fe.

In still another embodiment of the positive electrode active material for lithium ion batteries related to the invention, an average particle size of particles of the positive electrode active material is 2 to 8 μm, a specific surface area of the positive electrode active material is 0.3 to 1.8 m²/g, and the tap density of the positive electrode active material is 1.5 to 2.1 g/ ml.

In another aspect of the invention, the invention relates to a positive electrode for lithium ion batteries, which uses a positive electrode active material for lithium ion batteries related to the invention.

In still another aspect of the invention, the invention relates to a lithium ion battery that uses a positive electrode for lithium ion batteries related to the invention.

In further still another aspect of the invention, the invention relates to a precursor for positive electrode active material for lithium ion batteries which is composed of secondary particles made of at least lithium and transition metal and formed by flocculating primary particles. In the precursor for positive electrode active material, the variation in composition of transition metal that is a main component inside of secondary particles or between the secondary particles of the precursor for positive electrode active material, which is defined as a ratio of the absolute value of the difference between a composition ratio inside of the particles of or in a small area between the particles of the transition metal and a composition ratio in a bulk state to the composition ratio in the bulk state of the transition metal, is 5% or less.

The precursor for positive electrode active material for lithium ion batteries related to the invention includes, in an embodiment, lithium and transition metal as main component.

ADVANTAGEOUS EFFECT OF THE INVENTION

According to the invention, a positive electrode active material for lithium ion batteries, which realizes a lithium ion battery that is, while satisfying fundamental characteristics of a battery (capacity, efficiency, load characteristics), low in the resistance and excellent in the lifetime characteristics, is provided.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

(Constitution of Positive Electrode Active Material for Lithium Ion Batteries)

As a raw material of positive electrode active material for lithium ion batteries related to an embodiment of the invention, compounds useful as a positive electrode active material for general positive electrodes for lithium ion batteries can be broadly used. However, lithium-containing transition metal oxides such as lithium cobalt oxide (LiCoO₂), lithium nickel oxide (LiNiO₂) and lithium manganese oxide (LiMn₂O₄) can be particularly preferably used. Further, the transition metal in the lithium-containing transition metal oxide is preferred to be one or two or more kinds selected from the group consisting of Ni, Mn, Co and Fe. Further, a ratio of lithium to all metals in the lithium-containing transition metal oxide is preferable to be more than 1.0 and less than 1.3. This is because a stable crystal structure is difficult to maintain when the ratio is 1.0 or less, and high capacity of a battery cannot be secured when the ratio is 1.3 or more. A crystal structure of the positive electrode active material is not particularly restricted as long as it has a structure capable of inserting and removing lithium. However, a layer structure or spinel structure is preferable.

The variation in composition of the transition metal that is a main component inside of secondary particles or between secondary particles of the positive electrode active material for lithium ion batteries can be obtained in the following manner. That is, by use of an apparatus, capable of quantitatively analyzing a small area, such as a field-emission electron probe microanalyzer (FE-EPMA), contents of the respective elements present between secondary particles or inside of the secondary particle are measured, and, by assuming that a content ratio of each of elements to the content of all metals as a composition ratio of each of the elements, the variation in composition ratio is taken as an index. For example, when the contents of elements of Ni, Mn, Co and Fe respectively are N %, M %, C % and F %, and numerical values obtained by dividing by the respective atomic weights and thereby expressed in terms of mole are n, m, c and f, a composition ratio of Ni (molar ratio) is expressed by n/(n+m+c+f)×100 (%). The variation in composition of the transition metal that is a main component inside of the secondary particles or between the secondary particles of the positive electrode active material for lithium ion batteries is expressed by a ratio of the absolute value of the difference between the composition ratio inside of or in a small region between the particles of the transition metal and the composition ratio in a bulk state to the composition ratio in the bulk state of the transition metal obtained by ICP and the like. The variation in composition related to the invention is 5% or less. This is because when the variation in composition exceeds 5%, the lifetime characteristics are poor and the resistance when used in a battery becomes large.

Further, in the positive electrode active material for lithium ion batteries, it is preferable that an average particle size of the secondary particles is 2 to 8 μm, a specific surface area of the secondary particles is 0.3 to 1.8 m²/g, and the tap density of the secondary particles is 1.5 to 2.1 g/ml. This is because, when deviating from the ranges, high capacity becomes difficult to secure. Further, it is more preferable that an average particle size of the secondary particles is 5 to 7 μm, a specific surface area t of the secondary particles is 0.5 to 1.5 m²/g, and the tap density of the secondary particles is 1.6 to 2.1 g/ ml.

(Constitution of Positive Electrode for Lithium Ion Batteries and Lithium Ion Battery therewith)

The positive electrode for lithium ion batteries related to an embodiment of the invention has a structure where, for example, a positive electrode mixture prepared by mixing the positive electrode active material for lithium ion batteries having the above-described constitution, a conductive additive, and a binder is disposed on one or both surfaces of a current collector made of an aluminum foil. Further, the lithium ion battery related to an embodiment of the invention is provided with the positive electrode for lithium ion batteries having such a constitution.

(Constitution of Precursor for Positive Electrode Active Material for Lithium Ion Batteries)

The precursor for positive electrode active material for lithium ion batteries related to an embodiment of the invention is configured of at least lithium and transition metal and formed of secondary particles where primary particles are flocculated. The precursor for positive electrode active material for lithium ion batteries is a raw material of the positive electrode active material for lithium ion batteries. Similar to the positive electrode active material for lithium ion batteries, the variation in composition of transition metal that is a main component inside of the secondary particles or between the secondary particles, which is defined as a ratio of the absolute value of the difference between the composition ratio inside of the particles of transition metal or in a small region between the particles of the transition metal and the composition ratio in a bulk state of the transition metal to the composition ratio in the bulk state of the transition metal, is 5% or less.

(Method of Manufacturing Positive Electrode Active Material for Lithium Ion Batteries and Lithium Ion Batteries therewith)

Next, a method of manufacturing the positive electrode active material for lithium ion batteries related to an embodiment of the invention and lithium ion batteries therewith will be described.

Firstly, alkali hydroxide or alkali carbonate is added in an aqueous solution of a salt of transition metal that is a main component, to which a lithium compound is added, to prepare a precursor for positive electrode active material for lithium ion batteries. Alternatively, an aqueous solution of salt of transition metal that is a main component is added to a solution or suspension of alkali hydroxide or alkali carbonate to prepare a precursor for positive electrode active material for lithium ion batteries. In the case of former one, a region high in the pH tends to be locally formed to result in the variation in composition. Accordingly, the latter one is preferred.

Examples of the lithium compounds being added include, without restricting, lithium carbonate, lithium hydroxide, lithium oxide, lithium chloride, lithium nitrate, lithium sulfate, lithium hydrogen carbonate, lithium acetate, lithium fluoride, lithium bromide, lithium iodide and lithium peroxide. Among these, from the viewpoint of easy handling and cheapness, lithium carbonate is preferred.

Examples of aqueous solutions of salt of the transition metal (any one kind or two or more kinds of Ni, Mn, Co and Fe) include a nitrate solution, a sulfate solution, a chloride solution, or an acetate solution. In particular from the viewpoint of avoiding mingling of a negative ion, a nitrate solution is preferably used.

Examples of preferable alkali hydroxides include sodium hydroxide, potassium hydroxide and lithium hydroxide. Examples of preferable alkali carbonates include sodium carbonate, sodium hydrogen carbonate, potassium carbonate and lithium carbonate.

An addition speed of the aqueous solution of salt of transition metal that is a main component affects on the variation in composition of the transition metal that is a main component inside of or between the particles of the precursor for positive electrode active material for lithium ion batteries. That is, when the addition speed is high, local segregation is caused to be likely to generate the variation in composition. Accordingly, the aqueous solution is preferably added at a speed slow enough to be difficult to generate the local segregation. Further, it is also effective to conduct the reaction little by little by use of a micro-reactor or to promote the dispersion of a raw material by applying an ultrasonic vibration to a reactor during the reaction.

More specifically, a concentration of the aqueous solution of salt of transition metal is adjusted to a saturation concentration or a concentration close to the saturation concentration. In the case of saturation concentration, segregation may be caused by variation of the liquid temperature. Accordingly, a concentration close to the saturation concentration is preferred.

In a solution or suspension of alkali hydroxide or alkali carbonate, the concentration is determined by considering a reaction with the transition metal. An addition speed is different depending on a volume of the reactor. For example, when a reactor having a volume of 1 m³ is used, and 500 to 700 L of an aqueous solution of transition metal salt is added to 300 to 400 L of a suspension of alkali carbonate, an addition speed of the aqueous solution of transition metal salt is 2 to 5 L/min and more preferably 3 to 4 L/min. An addition time is 2 to 5 hr and more preferably 3 to 4 hr.

Next, the resulted precursor for positive electrode active material is, after drying, oxidized (firing in an oxidizing atmosphere) and pulverized under proper condition to obtain a powder of positive electrode active material. Further, in the step of drying, there is no problem in using a known drying method. However, for example, a method such as a fluid bed drying that can inhibit dried powder from flocculating can be preferably used, because particles of the precursor can be more uniformly dispersed. Still further, in the step of firing, a method that promotes contact between the powders during filling can be preferably used, because the reaction is more uniformly conducted. Further, also in the pulverization, there is no problem in using a known method. However, it is desirable to use dry air upon operation to avoid influence of moisture.

By making use of the positive electrode active material for lithium ion batteries obtained like this, according to a known method, a positive electrode for lithium ion batteries and lithium ion batteries therewith can be produced. In the lithium ion battery formed like this, the composition of the transition metal in the positive electrode active material is inhibited from fluctuating. Accordingly, high capacity, low resistance and long lifetime are realized. Therefore, in large devices that require these characteristics such as automobiles and road levelers, the lithium ion batteries are particularly useful.

EXAMPLES

Examples of the present invention, with comparative examples, will be described as follows, but the following examples are provided for better understanding of the present invention and its advantages, and intended to be non-limiting.

Example A

According to a wet method that uses an aqueous solution of nitrates of Ni, Mn and Co and lithium carbonate, carbonate that is a precursor was prepared. A molar ratio of charge amounts of Ni, Mn and Co at the time of production of the precursor was set to Ni:Mn:Co=1:1:1. The mixture was, after drying, oxidized to form a positive electrode material.

More specifically, in a stirring bath with a propeller blade, lithium carbonate was suspended in pure water, the pH thereof was adjusted to 7, an aqueous solution of nitrates was introduced, and, after the introduction was completed at the pH 4, the stirring was continued for 2 hr. In order to inhibit the variation from occurring during the reaction, ultrasonic dispersion was applied during the stirring.

The prepared precursor was dried as it is without washing. A fluid bed dryer was used to inhibit the particles from sticking fast. An average particle size of dry powder was 10 μm.

This was filled in a sagger and fired. Upon filling, the sagger was vibrated for particles to come into contact with each other. The firing was conducted in air at 800° C. for 10 hr.

After firing, a pulverizer in which the particles collide with each other to pulverize was used. In order to eliminate influence of moisture, the step of pulverizing was conducted under an environment of dry air.

Comparative Example A

After powders of nickel oxide, manganese oxide and cobalt oxide and lithium hydroxide were wet mixed, the mixture was spray dried to prepare dry powder, and the dry powder was oxidized to prepare a positive electrode material. A molar ratio of charge amounts of Ni, Mn and Co at the time of mixing was set to Ni:Mn:Co=1:1:1.

More specifically, the respective raw materials measured in accordance with the ratio of charge amounts were mixed with water in a wet ball mill. The mixing time was set to 6 hr. Thereafter, a raw material slurry from which balls were removed was spray dried to remove moisture, thereby a dry powder was obtained. An average particle size of the dry powder was 30 μm.

The dry powder was filled in a sagger by tapping and fired at 800° C. for 10 hr in air. After firing, the powder was pulverized with a ball mill.

Contents of Li, Ni, Mn and Co in all positive electrode materials were measured with an inductively-coupled plasma optical emission spectrometer (ICP-OES) and thereby the ratio of the transition metals was confirmed to be the same as the ratio of charge amounts. (The composition ratio in a bulk state was 33.3% by mole for each of Ni, Mn and Co.)

Contents of the respective elements inside of the secondary particles and between the secondary particles were measured for each of the positive electrode materials by FE-EPMA, and results thereof are shown in Tables 1 and 2. Upon measurement, 3 positions inside of the secondary particle and 3 positions between the secondary particles were measured. Each of the contents was calculated in terms of mole and recalculated as a composition ratio. The composition ratio was expressed by a ratio of a molar amount of a specified element and a total molar amount of all metals. As the variation in composition, a numerical value obtained by dividing the absolute value of the difference between the composition ratio and the composition ratio of a bulk measured by ICP-OES by the composition ratio of bulk was used.

TABLE 1 Composition Variation in Content (%) ratio (mole %) composition (%) Ni Mn Co Ni Mn Co Ni Mn Co Example A 1 20.3 19.0 20.3 33.4 33.4 33.2 0.1 0.1 0.3 2 20.5 18.9 20.0 33.8 33.3 32.9 1.5 0.1 1.4 3 20.2 19.5 20.5 32.9 33.9 33.2 1.4 1.7 0.3 Comparative 4 21.0 17.3 18.5 36.3 31.9 31.8 8.8 4.3 4.5 example A 5 18.5 18.7 18.5 32.5 35.1 32.4 2.5 5.3 2.9 6 19.8 20.2 20.0 32.3 35.2 32.5 3.1 5.6 2.5

TABLE 2 Composition Variation in Content (%) ratio (mole %) composition (%) Ni Mn Co Ni Mn Co Ni Mn Co Example A 7 20.5 19.0 20.6 33.4 33.1 33.5 0.3 0.7 0.4 8 20.9 18.9 20.3 34.1 32.9 33.0 2.3 1.2 1.1 9 20.2 19.7 20.5 32.8 34.1 33.1 1.7 2.4 0.7 Comparative 10 21.2 17.2 18.7 36.4 31.6 32.0 9.3 5.3 4.0 example A 11 18.3 19.0 18.5 32.1 35.6 32.3 3.7 6.8 3.1 12 19.8 20.2 19.7 32.4 35.4 32.2 2.6 6.1 3.5

Further, as an average particle size, a 50% diameter in a particle size distribution according to a laser diffraction method was used, as a specific surface area, a BET value was used, and as a tap density, a density obtained after 200 times of tapping was used. The positive electrode material, a conductive material and a binder were weighed at a ratio of 85:8:7. In a solution obtained by dissolving the binder in an organic solvent (N-methyl pyrrolidone), the material and conductive material were mixed to form a slurry. The slurry was coated on an aluminum foil and, after drying, pressed to form a positive electrode. A 2032 coin cell for use in evaluation, in which Li is used as a counter electrode was prepared, and, with a solution obtained by dissolving 1M-LiPF6 in EC-DMC (1:1) as an electrolytic solution, the charge and discharge operation was conducted under the charge condition of 4.3 V and the discharge condition of 3.0 V. Initial capacity and initial efficiency (discharge amount/ charge amount) were confirmed under the charge/ discharge at 0.1 C. Further, the resistance was estimated from a decrease in voltage from charge end to discharge start. As the lifetime, the capacity retention rate after 30 cycles at room temperature was confirmed. These results are shown in Table 3.

TABLE 3 Average Specific Tap particle surface den- Capac- Effi- Resis- Life- size area sity ity ciency tance time μm m²/g g/ml mAh/g % mΩ % Exam- 5.5 1.24 2.0 155 90.3 0.5 98 ple A Compar- 8.3 1.08 2.0 150 87.6 1.1 92 ative exam- ple A

Example B

According to a wet method that uses an aqueous solution of nitrates of Ni, Mn and Fe and lithium carbonate, carbonate that is a precursor was prepared. A molar ratio of charge amounts of Ni, Mn and Fe at the time of production of the precursor was set to Ni:Mn:Fe=6:2:2. The mixture was, after drying, oxidized to form a positive electrode material.

More specifically, in a stirring bath with a propeller blade, lithium carbonate was suspended in pure water, the pH was adjusted to 7, an aqueous solution of nitrates was introduced, and, after the introduction was completed at the pH 4, the stirring was continued for 2 hr. In order to inhibit the variation from occurring during the reaction, ultrasonic dispersion was applied during the stirring.

The prepared precursor was dried as it is without washing. A fluid bed dryer was used to inhibit the particles from sticking fast. An average particle size of dry powder was 10 μm.

This was filled in a sagger and fired. Upon filling, the sagger was vibrated for particles to come into contact with each other. The firing was conducted in air at 800° C. for 10 hr.

After firing, a pulverizer in which the particles collide with each other to pulverize was used. In order to eliminate influence of moisture, the step of pulverizing was conducted under an environment of dry air.

Comparative Example B

After powders of nickel oxide, manganese oxide and iron oxide and lithium hydroxide were wet mixed, the mixture was spray dried to prepare dry powder, and the dry powder was oxidized to prepare a positive electrode material. A molar ratio of charge amounts of Ni, Mn and Fe at the time of mixing was set to Ni:Mn:Fe=6:2:2.

More specifically, the respective raw materials weighed in accordance with the ratio of charge amounts were mixed with water in a wet ball mill. The mixing time was set to 6 hr. Thereafter, a raw material slurry from which balls were removed was spray dried to remove moisture, thereby a dry powder was obtained. An average particle size of the dry powder was 30 μm.

The dry powder was filled in a sagger by tapping and fired at 800° C. for 10 hr in air. After firing, the pulverization was conducted with a ball mill.

Contents of Li, Ni, Mn and Fe in all positive electrode materials were measured with an inductively-coupled plasma optical emission spectrometer (ICP-OES) and thereby the ratio of the transition metals was confirmed to be the same as the ratio of charge amounts. (The composition ratio in a bulk state was Ni:Mn:Fe=6:2:2 by molar ratio of Ni, Mn and Fe.)

Contents of the respective elements inside of the secondary particles and between the secondary particles were measured for each of the positive electrode materials by FE-EPMA, and results thereof are shown in Tables 4 and 5. Upon measurement, 3 positions inside of the secondary particle and 3 positions between the secondary particles were measured. Each of the contents was calculated in terms of mole and recalculated as a composition ratio. The composition ratio was expressed by a ratio of a molar amount of a specified element to a total molar amount of all metals. As the variation in composition, a numerical value obtained by dividing the absolute value of the difference between the composition ratio and the composition ratio of a bulk measured by ICP-OES by the composition ratio of bulk was used.

TABLE 4 Composition Variation in Content (%) ratio (mole %) composition (%) Ni Mn Fe Ni Mn Fe Ni Mn Fe Example B 1 35.7 11.0 11.2 60.3 19.8 19.9 0.4 0.8 0.6 2 36.2 11.1 11.1 60.6 19.9 19.5 1.0 0.7 2.3 3 36.0 10.8 11.2 60.7 19.5 19.8 1.2 2.7 0.8 Comparative 4 39.0 11.0 10.8 62.8 18.9 18.3 4.7 5.4 8.6 example B 5 34.4 11.5 10.8 59.2 21.2 19.6 1.2 5.8 2.2 6 35.6 12.0 11.2 59.1 21.3 19.6 1.4 6.5 2.2

TABLE 5 Composition Variation in Content (%) ratio (mole %) composition (%) Ni Mn Fe Ni Mn Fe Ni Mn Fe Example B 7 36.2 11.2 11.5 60.1 19.9 20.0 0.1 0.7 0.3 8 35.8 10.9 11.0 60.7 19.7 19.6 1.1 1.3 2.0 9 36.5 11.3 11.4 60.3 19.9 19.8 0.5 0.3 1.1 Comparative 10 38.2 10.8 11.0 62.3 18.8 18.9 3.9 5.9 5.7 example B 11 34.8 11.3 12.1 58.4 20.3 21.3 2.7 1.3 6.7 12 36.2 12.3 11.9 48.5 21.3 20.2 2.4 6.2 1.1

Further, as an average particle size, a 50% diameter in a particle size distribution according to a laser diffraction method was used, as a specific surface area, a BET value was used, and as a tap density, a density obtained after 200 times of tapping was used. The positive electrode material, a conductive material and a binder were weighed at a ratio of 85:8:7. In a solution obtained by dissolving the binder in an organic solvent (N-methyl pyrrolidone), the material and conductive material were mixed to form a slurry. The slurry was coated on an aluminum foil and, after drying, pressed to form a positive electrode. A 2032 coin cell for use in evaluation, in which Li is used as a counter electrode was prepared, and, with a solution obtained by dissolving 1M-LiPF6 in EC-DMC (1:1) as an electrolytic solution, the charge and discharge operation was conducted under the charge condition of 4.3 V and the discharge condition of 3.0 V. Initial capacity and initial efficiency (discharge amount/ charge amount) were confirmed under the charge/ discharge at 0.1 C. Further, the resistance was estimated from a decrease in voltage from charge end to discharge start. As the lifetime, the capacity retention rate after 30 cycles at room temperature was confirmed. These results are shown in Table 6.

TABLE 6 Average Specific Tap particle surface den- Capac- Effi- Resis- Life- size area sity ity ciency tance time μm m²/g g/ml mAh/g % mΩ % Exam- 6.2 1.02 2.0 167 90.2 0.8 96 ple B Compar- 9.5 1.16 2.0 155 88.8 1.6 89 ative exam- ple B 

1. A positive electrode active material for lithium ion batteries, which is composed of at least lithium and transition metal, wherein the variation in the composition of transition metal that is a main component inside of particles of or between particles of the positive electrode active material, which is defined as a ratio of the absolute value of the difference between a composition ratio inside of the particles of or in a small area between the particles of the transition metal and a composition ratio in a bulk state to the composition ratio in a bulk state of the transition metal, is 5% or less.
 2. The positive electrode active material for lithium ion batteries of claim 1, wherein the positive electrode active material is a lithium-containing transition metal oxide.
 3. The positive electrode active material for lithium ion batteries of claim 2, wherein the transition metal in the lithium-containing transition metal oxide is at least one or two or more kinds selected from the group consisting of Ni, Mn, Co and Fe.
 4. The positive electrode active material for lithium. ion batteries of any one of claims 1 to 3, wherein an average particle size of particles of the positive electrode active material is 2 to 8 μm, a specific surface area of the positive electrode active material is 0.3 to 1.8 m²/g, and the tap density of the positive electrode active material is 1.5 to 2.1 g/ml.
 5. A positive electrode for lithium ion batteries, comprising a positive electrode active material for lithium ion batteries of any one of claims 1 to
 3. 6. A lithium ion battery comprising a positive electrode for lithium ion batteries of claim
 5. 7. A precursor for positive electrode active material for lithium ion batteries, which is composed of secondary particles made of at least lithium and transition metal and formed by flocculating primary particles, wherein the variation in composition of transition metal that is a main component inside of secondary particles or between the secondary particles of the precursor for positive electrode active material, which is defined as a ratio of the absolute value of the difference between a composition ratio inside of the particles of or in a small area between the particles of the transition metal and a composition ratio in a bulk state to the composition ratio in the bulk state of the transition metal, is 5% or less.
 8. The precursor for positive electrode active material for lithium ion batteries of claim 7, including lithium and transition metal as main component. 